Comparative Evaluation of the Cyclic Fatigue Resistance of Thermally Treated Nickel-Titanium (Ni-Ti) instruments at Varying Temperatures

N.A.

Article Details

Comparative Evaluation of the Cyclic Fatigue Resistance of Thermally Treated Nickel-Titanium (Ni-Ti) instruments at Varying Temperatures

Authors:

N.A.

Publisher:

Ataturk University

Main Topics:

Endodonti

Journal:

Current Research in Dental Sciences Vol.34 Issue 2, pp.89-93

Document Type:

Article

Publication Date:

4/2024

Document Language:

English

Document ID (Org No.):

2001316888

pISSN:

2822-2555

Keywords:

Abstract:

 Objective: This study aimed to evaluate the stationary cyclic fatigue resistance CFR of three endodontic instrument systems at varying temperatures 20  1C and 37  1C.. Methods: Ninety endodontic instruments from three instrument systems HyFlex CM, 2Shape and Hero Gold of constant tip size and taper 25.04 were selected for this study. These systems were broadly, divided into three groups n30: Group 1 Hyflex CM, Group 2 2Shape and Group 3 Hero Gold. Each group was further subdivided into two subgroups based on the temperature variable used. The endodontic instruments were subjected to stationary cyclic fatigue testing at 20  1C and 37  1C using a stainless-steel block with an artificial canal. The number of cycles to failure NCF were recorded Results: Data was analysed using two-way ANOVA and Tukey post-hoc tests at a 95 confidence level. The instrument type and temperature variable significantly affect the NCF values. The observed NCF of the tested instruments was higher at 2010 C compared to its values at 3710 C and was statistically significant. The HyFlex CM group exhibited the highest CFR at 2010 C, while at 3710 C the Hero Gold instruments exhibited a higher CFR. Conclusion: It can be inferred that Hero Gold instruments exhibited superior clinical performance when compared with Hyflex CM and 2Shape rotary instruments at body temperature 3710 C. The observed reduction in the NCF when increasing the temperature ranges between 30.29 - 71.27.. Keywords: Cyclic Fatigue Resistance, Hero Gold, Hyflex CM, Nickel-Titanium, Stationary Fatigue, and 2Shape ÖZ Amaç: Bu çalışma, üç endodontik alet sisteminin değişen sıcaklıklarda 20  1C ve 37  1C sabit yorulma direncini CFR değerlendirmeyi amaçladı Yöntemler: Bu çalışma için sabit uç boyutu ve konikliğe 25,04 sahip üç alet sisteminden HyFlex CM, 2Shape ve Hero Gold doksan endodontik alet seçildi. Bu sistemler genel olarak üç gruba ayrıldı: Grup 1 Hyflex CM, Grup 2 2Shape ve Grup 3 Hero Gold. Her grup ayrıca kullanılan sıcaklık değişkenine bağlı olarak iki alt gruba bölündü. Endodontik aletler, yapay kanallı paslanmaz çelik bir blok kullanılarak 20  1C ve 37  1Cde sabit döngüsel yorulma testine tabi tutuldu. Arızaya kadar olan döngü sayısı NCF kaydedildi Bulgular: Veriler, iki yönlü ANOVA ve Tukey post-hoc testleri kullanılarak 95 güven seviyesinde analiz edildi. Alet tipi ve sıcaklık değişkeni NCF değerlerini önemli ölçüde etkiler. Test edilen cihazların gözlenen NCFsi 2010 Cde 3710 Cdeki değerlerine göre daha yüksekti ve istatistiksel olarak anlamlıydı. HyFlex CM grubu en yüksek CFRyi 2010 Cde sergilerken, 3710 Cde Hero Gold aletleri daha yüksek bir CFR sergiledi Sonuç: Hero Gold aletlerinin vücut sıcaklığında 3710 C Hyflex CM ve 2Shape döner aletlerle karşılaştırıldığında üstün klinik performans sergilediği söylenebilir. Sıcaklık artırıldığında NCFde gözlenen azalma 30,29 - 71,27 arasında değişmektedir. Anahtar Kelimeler: Cyclic Fatigue Resistance, Hero Gold, Hyflex CM, Nickel-Titanium, Stationary Fatigue, and 2Shape.

 Objective: This study aimed to evaluate the stationary cyclic fatigue resistance CFR of three endodontic instrument systems at varying temperatures 20  1C and 37  1C.. Methods: Ninety endodontic instruments from three instrument systems HyFlex CM, 2Shape and Hero Gold of constant tip size and taper 25.04 were selected for this study. These systems were broadly, divided into three groups n30: Group 1 Hyflex CM, Group 2 2Shape and Group 3 Hero Gold. Each group was further subdivided into two subgroups based on the temperature variable used. The endodontic instruments were subjected to stationary cyclic fatigue testing at 20  1C and 37  1C using a stainless-steel block with an artificial canal. The number of cycles to failure NCF were recorded Results: Data was analysed using two-way ANOVA and Tukey post-hoc tests at a 95 confidence level. The instrument type and temperature variable significantly affect the NCF values. The observed NCF of the tested instruments was higher at 2010 C compared to its values at 3710 C and was statistically significant. The HyFlex CM group exhibited the highest CFR at 2010 C, while at 3710 C the Hero Gold instruments exhibited a higher CFR. Conclusion: It can be inferred that Hero Gold instruments exhibited superior clinical performance when compared with Hyflex CM and 2Shape rotary instruments at body temperature 3710 C. The observed reduction in the NCF when increasing the temperature ranges between 30.29 - 71.27.. Keywords: Cyclic Fatigue Resistance, Hero Gold, Hyflex CM, Nickel-Titanium, Stationary Fatigue, and 2Shape ÖZ Amaç: Bu çalışma, üç endodontik alet sisteminin değişen sıcaklıklarda 20  1C ve 37  1C sabit yorulma direncini CFR değerlendirmeyi amaçladı Yöntemler: Bu çalışma için sabit uç boyutu ve konikliğe 25,04 sahip üç alet sisteminden HyFlex CM, 2Shape ve Hero Gold doksan endodontik alet seçildi. Bu sistemler genel olarak üç gruba ayrıldı: Grup 1 Hyflex CM, Grup 2 2Shape ve Grup 3 Hero Gold. Her grup ayrıca kullanılan sıcaklık değişkenine bağlı olarak iki alt gruba bölündü. Endodontik aletler, yapay kanallı paslanmaz çelik bir blok kullanılarak 20  1C ve 37  1Cde sabit döngüsel yorulma testine tabi tutuldu. Arızaya kadar olan döngü sayısı NCF kaydedildi Bulgular: Veriler, iki yönlü ANOVA ve Tukey post-hoc testleri kullanılarak 95 güven seviyesinde analiz edildi. Alet tipi ve sıcaklık değişkeni NCF değerlerini önemli ölçüde etkiler. Test edilen cihazların gözlenen NCFsi 2010 Cde 3710 Cdeki değerlerine göre daha yüksekti ve istatistiksel olarak anlamlıydı. HyFlex CM grubu en yüksek CFRyi 2010 Cde sergilerken, 3710 Cde Hero Gold aletleri daha yüksek bir CFR sergiledi Sonuç: Hero Gold aletlerinin vücut sıcaklığında 3710 C Hyflex CM ve 2Shape döner aletlerle karşılaştırıldığında üstün klinik performans sergilediği söylenebilir. Sıcaklık artırıldığında NCFde gözlenen azalma 30,29 - 71,27 arasında değişmektedir. Anahtar Kelimeler: Cyclic Fatigue Resistance, Hero Gold, Hyflex CM, Nickel-Titanium, Stationary Fatigue, and 2Shape.

 Objective: This study aimed to evaluate the stationary cyclic fatigue resistance CFR of three endodontic instrument systems at varying temperatures 20  1C and 37  1C.. Methods: Ninety endodontic instruments from three instrument systems HyFlex CM, 2Shape and Hero Gold of constant tip size and taper 25.04 were selected for this study. These systems were broadly, divided into three groups n30: Group 1 Hyflex CM, Group 2 2Shape and Group 3 Hero Gold. Each group was further subdivided into two subgroups based on the temperature variable used. The endodontic instruments were subjected to stationary cyclic fatigue testing at 20  1C and 37  1C using a stainless-steel block with an artificial canal. The number of cycles to failure NCF were recorded Results: Data was analysed using two-way ANOVA and Tukey post-hoc tests at a 95 confidence level. The instrument type and temperature variable significantly affect the NCF values. The observed NCF of the tested instruments was higher at 2010 C compared to its values at 3710 C and was statistically significant. The HyFlex CM group exhibited the highest CFR at 2010 C, while at 3710 C the Hero Gold instruments exhibited a higher CFR. Conclusion: It can be inferred that Hero Gold instruments exhibited superior clinical performance when compared with Hyflex CM and 2Shape rotary instruments at body temperature 3710 C. The observed reduction in the NCF when increasing the temperature ranges between 30.29 - 71.27.. Keywords: Cyclic Fatigue Resistance, Hero Gold, Hyflex CM, Nickel-Titanium, Stationary Fatigue, and 2Shape ÖZ Amaç: Bu çalışma, üç endodontik alet sisteminin değişen sıcaklıklarda 20  1C ve 37  1C sabit yorulma direncini CFR değerlendirmeyi amaçladı Yöntemler: Bu çalışma için sabit uç boyutu ve konikliğe 25,04 sahip üç alet sisteminden HyFlex CM, 2Shape ve Hero Gold doksan endodontik alet seçildi. Bu sistemler genel olarak üç gruba ayrıldı: Grup 1 Hyflex CM, Grup 2 2Shape ve Grup 3 Hero Gold. Her grup ayrıca kullanılan sıcaklık değişkenine bağlı olarak iki alt gruba bölündü. Endodontik aletler, yapay kanallı paslanmaz çelik bir blok kullanılarak 20  1C ve 37  1Cde sabit döngüsel yorulma testine tabi tutuldu. Arızaya kadar olan döngü sayısı NCF kaydedildi Bulgular: Veriler, iki yönlü ANOVA ve Tukey post-hoc testleri kullanılarak 95 güven seviyesinde analiz edildi. Alet tipi ve sıcaklık değişkeni NCF değerlerini önemli ölçüde etkiler. Test edilen cihazların gözlenen NCFsi 2010 Cde 3710 Cdeki değerlerine göre daha yüksekti ve istatistiksel olarak anlamlıydı. HyFlex CM grubu en yüksek CFRyi 2010 Cde sergilerken, 3710 Cde Hero Gold aletleri daha yüksek bir CFR sergiledi Sonuç: Hero Gold aletlerinin vücut sıcaklığında 3710 C Hyflex CM ve 2Shape döner aletlerle karşılaştırıldığında üstün klinik performans sergilediği söylenebilir. Sıcaklık artırıldığında NCFde gözlenen azalma 30,29 - 71,27 arasında değişmektedir. Anahtar Kelimeler: Cyclic Fatigue Resistance, Hero Gold, Hyflex CM, Nickel-Titanium, Stationary Fatigue, and 2Shape.

 Objective: This study aimed to evaluate the stationary cyclic fatigue resistance CFR of three endodontic instrument systems at varying temperatures 20  1C and 37  1C.. Methods: Ninety endodontic instruments from three instrument systems HyFlex CM, 2Shape and Hero Gold of constant tip size and taper 25.04 were selected for this study. These systems were broadly, divided into three groups n30: Group 1 Hyflex CM, Group 2 2Shape and Group 3 Hero Gold. Each group was further subdivided into two subgroups based on the temperature variable used. The endodontic instruments were subjected to stationary cyclic fatigue testing at 20  1C and 37  1C using a stainless-steel block with an artificial canal. The number of cycles to failure NCF were recorded Results: Data was analysed using two-way ANOVA and Tukey post-hoc tests at a 95 confidence level. The instrument type and temperature variable significantly affect the NCF values. The observed NCF of the tested instruments was higher at 2010 C compared to its values at 3710 C and was statistically significant. The HyFlex CM group exhibited the highest CFR at 2010 C, while at 3710 C the Hero Gold instruments exhibited a higher CFR. Conclusion: It can be inferred that Hero Gold instruments exhibited superior clinical performance when compared with Hyflex CM and 2Shape rotary instruments at body temperature 3710 C. The observed reduction in the NCF when increasing the temperature ranges between 30.29 - 71.27.. Keywords: Cyclic Fatigue Resistance, Hero Gold, Hyflex CM, Nickel-Titanium, Stationary Fatigue, and 2Shape ÖZ Amaç: Bu çalışma, üç endodontik alet sisteminin değişen sıcaklıklarda 20  1C ve 37  1C sabit yorulma direncini CFR değerlendirmeyi amaçladı Yöntemler: Bu çalışma için sabit uç boyutu ve konikliğe 25,04 sahip üç alet sisteminden HyFlex CM, 2Shape ve Hero Gold doksan endodontik alet seçildi. Bu sistemler genel olarak üç gruba ayrıldı: Grup 1 Hyflex CM, Grup 2 2Shape ve Grup 3 Hero Gold. Her grup ayrıca kullanılan sıcaklık değişkenine bağlı olarak iki alt gruba bölündü. Endodontik aletler, yapay kanallı paslanmaz çelik bir blok kullanılarak 20  1C ve 37  1Cde sabit döngüsel yorulma testine tabi tutuldu. Arızaya kadar olan döngü sayısı NCF kaydedildi Bulgular: Veriler, iki yönlü ANOVA ve Tukey post-hoc testleri kullanılarak 95 güven seviyesinde analiz edildi. Alet tipi ve sıcaklık değişkeni NCF değerlerini önemli ölçüde etkiler. Test edilen cihazların gözlenen NCFsi 2010 Cde 3710 Cdeki değerlerine göre daha yüksekti ve istatistiksel olarak anlamlıydı. HyFlex CM grubu en yüksek CFRyi 2010 Cde sergilerken, 3710 Cde Hero Gold aletleri daha yüksek bir CFR sergiledi Sonuç: Hero Gold aletlerinin vücut sıcaklığında 3710 C Hyflex CM ve 2Shape döner aletlerle karşılaştırıldığında üstün klinik performans sergilediği söylenebilir. Sıcaklık artırıldığında NCFde gözlenen azalma 30,29 - 71,27 arasında değişmektedir. Anahtar Kelimeler: Cyclic Fatigue Resistance, Hero Gold, Hyflex CM, Nickel-Titanium, Stationary Fatigue, and 2Shape.

Article Details

Comparative Evaluation of the Cyclic Fatigue Resistance of Thermally Treated Nickel-Titanium (Ni-Ti) instruments at Varying Temperatures

Authors: N.A.

Publisher: Ataturk University

Main Topics: Endodonti

Journal: Current Research in Dental Sciences Vol.34 Issue 2, pp.89-93

Document Type: Article

Publication Date: 4/2024

Document Language: English

Document ID (Org No.): 2001316888

pISSN: 2822-2555

Cyclic Fatigue Resistance

Hero Gold

Hyflex CM

Nickel-Titanium

Stationary Fatigue

Issues

Authors:

N.A.

Publisher:

Ataturk University

Main Topics:

Endodonti

Journal:

Current Research in Dental Sciences Vol.34 Issue 2, pp.89-93

Document Type:

Article

Publication Date:

4/2024

Document Language:

English

Document ID (Org No.):

2001316888

pISSN:

2822-2555