Correction des Défauts de Sablage D’un Verre par Déposition de Couches Minces de Silice et de PVB

Hind Laouamri; Mostafa Kolli; Nourredine Bouaouadja

doi:10.12816/0010609

Article Details

Correction des Défauts de Sablage D’un Verre par Déposition de Couches Minces de Silice et de PVB

Authors:

Hind Laouamri | Mostafa Kolli | Nourredine Bouaouadja

Publisher:

Kasdi Merbah University of Ouargla

Main Topics:

Physics

Journal:

Ḥawliyāt al-ʻUlūm wa-al-Tiknūlūjiyā 2013 Vol.5 Issue 2, pp.136-142

Document Type:

Article

Publication Date:

10/2013

Document Language:

French

Document ID (Org No.):

62359

Frequency:

Bi-Annual

pISSN:

21700672

DOI:

10.12816/0010609

Descriptors:

Keywords:

Abstract:

 Le but de notre travail est de corriger les défauts de surface causés par les impacts de particules de sable sur la surface d’un verre en déposant une couche de silice par voie sol-gel. Pour cela, nous avons sablé des échantillons en verre sodo-calcique avec différentes masses et nous avons déposé par la suite des couches minces transparentes. Au cours du sablage, lorsque la masse projetée augmente, le nombre de défauts et leurs tailles augmentent. La transmission optique T accuse une chute importante. Elle passe de 91,4% (valeur initiale) à 12.96% pour un état sablé avec une masse de 200g. Parallèlement, la rugosité totale Rt augmente d’environ 0.65 µm (état initial) jusqu’à 11,75 μm. Pour corriger les défauts de sablage, nous avons synthétisé une solution sol-gel à base de précurseurs de SiO2 (TEOS). Après séchage dans une étuve à 50°C durant 30 min, les échantillons sont recuits à 550°C pendant 1 heure. Nous avons constaté que l’épaisseur moyenne des couches déposées est très faible (380-450) nm. Après revêtement avec des couches de SiO2, nous avons constaté une nette amélioration de T qui passe de 12.96 à 42.98%, et parallèlement une diminution de Rt. Cette amélioration de la transmission est jugée très insuffisante devant la rugosité totale. Pour l’augmenter encore, nous avons dissolu un polymère (PVB) dans le solvant (DMF) et nous l’avons déposé sur la couche de SiO2. Après séchage à 60°C pendant 24 h, l’épaisseur moyenne obtenue cette fois-ci est de 18,7 µm. Cette dernière valeur dépasse largement les valeurs de la rugosité totale. La transmission optique augmente encore et passe à 88 % pour le cas de sablage le plus défavorable (Mp = 200 g).

 The aim of our work is to correct surface defects caused by the impacts of sand particles on the surface of a glass. The procedure consists to deposit a thin layer of silica by sol-gel technique. For this, soda-lime glass samples were sandblasted with different masses and subsequently thin transparent films were filed. The results show that when the sand mass increases, the number of defects and their size increase also. Optical transmission shows a significant drop. It changes from 91.4% (initial value) to 12.96% for a mass of 200g. Meanwhile, the total roughness increases from 0.65 to 11.75 µm. To correct the sandblasting defects, we synthesized a sol-gel solution based precursors SiO2 (TEOS) and we coated the samples. After drying in an oven heated at 50°C for 30 min, the samples were annealed at 550°C for 1 hour. The average thickness obtained for the deposited layers is very low (380-450) nm. Nevertheless, a significant improvement in the optical transmission has been observed (increase from 12.96 to 42.98%). But this last value is not sufficient. To increase again the thickness, another method is adopted. A polymer (PVB) is dissolved in an adequate solvent (DMF) and the obtained solution is deposited on the SiO2 layers. After drying at 60°C for 24 h, the average thickness obtained in this case is important enough (18.7 µm). This value exceeds the values of the total roughness. Finally, the optical transmission increases significantly up to 88% for Mp = 200 g.

Article Details

Correction des Défauts de Sablage D’un Verre par Déposition de Couches Minces de Silice et de PVB

Authors:

Hind Laouamri | Mostafa Kolli | Nourredine Bouaouadja

Publisher:

Kasdi Merbah University of Ouargla

Main Topics:

Physics

Journal:

Ḥawliyāt al-ʻUlūm wa-al-Tiknūlūjiyā 2013 Vol.5 Issue 2, pp.136-142

Document Type:

Article

Publication Date:

10/2013

Document Language:

French

Document ID (Org No.):

62359

Frequency:

Bi-Annual

pISSN:

21700672

DOI:

10.12816/0010609

Descriptors:

GLASS

SOIL EROSION

MOLECULES

ROUGHNESS

DEFECTS

Verre

Erosion

Technique Sol Gel

Transmission Optique

Rugosité

Glass

Erosion

Sol-Gel Technique

Optical Transmission

Roughness

Issues

Article Details

Authors: Hind Laouamri | Mostafa Kolli | Nourredine Bouaouadja

Publisher: Kasdi Merbah University of Ouargla

Main Topics: Physics

Journal: Ḥawliyāt al-ʻUlūm wa-al-Tiknūlūjiyā 2013 Vol.5 Issue 2, pp.136-142

Document Type: Article

Publication Date: 10/2013

Document Language: French

Document ID (Org No.): 62359

Frequency: Bi-Annual

pISSN: 21700672

DOI: 10.12816/0010609

Descriptors:

Issues

Authors:

Hind Laouamri | Mostafa Kolli | Nourredine Bouaouadja

Publisher:

Kasdi Merbah University of Ouargla

Main Topics:

Physics

Journal:

Ḥawliyāt al-ʻUlūm wa-al-Tiknūlūjiyā 2013 Vol.5 Issue 2, pp.136-142

Document Type:

Article

Publication Date:

10/2013

Document Language:

French

Document ID (Org No.):

62359

Frequency:

Bi-Annual

pISSN:

21700672

DOI:

10.12816/0010609